Lithium Ion Battery, Integrated Circuit and Method of Manufacturing a Lithium Ion Battery

ABSTRACT

A lithium ion battery includes a first substrate having a first main surface, and a lid including a conductive cover element, the lid being attached to the first main surface. A cavity is formed between the first substrate and the lid. The battery further includes an electrolyte disposed in the cavity. An anode of the battery includes a component made of a semiconductor material and is formed at the first substrate, and a cathode of the battery is formed at the lid.

BACKGROUND

With the increased use of portable electronic devices such as notebooks,portable telephones, cameras and others and with the increased use ofcurrent-driven automobiles, lithium ion secondary batteries with highenergy density have attracted increasing attention as a power source.

Further, attempts are made for providing semiconductor devices orsemiconductor-based devices having an integrated power source.

Lithium ion secondary batteries typically include a cathode comprising alithium-containing transition metal oxide or the like, an anodetypically made of a carbon material and a non-aqueous electrolytecontaining a lithium salt as well as a separator situated between theanode and the cathode.

In order to meet the increasing demands on capacity and performance, newconcepts for lithium batteries that can be manufactured in a simplemanner are desirable.

SUMMARY

According to an embodiment, a lithium ion battery comprises a firstsubstrate having a first main surface, a lid comprising a conductivecover element, the lid being attached to the first main surface, and acavity formed between the first substrate and the lid. An electrolyte isdisposed in the cavity. The lithium ion battery further includes ananode comprising a component made of a semiconductor material at thefirst substrate, and a cathode at the lid.

According to a further embodiment, an integrated circuit is formed in afirst semiconductor substrate having a first main surface. Theintegrated circuit comprises a lithium ion battery and further includesa lid comprising a conductive cover element, the lid being attached tothe first main surface, a cavity formed between the first semiconductorsubstrate and the lid, and an electrolyte disposed in the cavity. Thelithium ion battery further includes an anode comprising a componentmade of a semiconductor material at the first semiconductor substrate,and a cathode of the battery at the lid.

According to a further embodiment, a method of manufacturing a lithiumion battery comprises attaching a lid to a first main surface of a firstsubstrate, the lid comprising a conductive cover element, forming acavity between the lid and the first substrate, forming an anodecomprising a component made of a semiconductor material at the firstsubstrate, forming a cathode at the lid, and filling an electrolyte intothe cavity.

Those skilled in the art will recognize additional features andadvantages upon reading the following detailed description, and uponviewing the accompanying drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

The accompanying drawings are included to provide a furtherunderstanding of embodiments of the invention and are incorporated inand constitute a part of this specification. The drawings illustrate theembodiments of the present invention and together with the descriptionserve to explain the principles. Other embodiments of the invention andmany of the intended advantages will be readily appreciated, as theybecome better understood by reference to the following detaileddescription. The elements of the drawings are not necessarily to scalerelative to each other. Like reference numbers designate correspondingsimilar parts.

FIG. 1A illustrates a cross-sectional view of an integrated circuitaccording to an embodiment;

FIGS. 1B to 1C illustrate steps of a method for manufacturing a batteryaccording to an embodiment;

FIGS. 1D and 1E illustrate general modifications of the battery;

FIG. 2A shows a cross-sectional view of an integrated circuit accordingto a further embodiment;

FIGS. 2B to 2F illustrate steps of a method of manufacturing a batteryaccording to an embodiment; and

FIG. 3 illustrates a method of manufacturing a battery.

DETAILED DESCRIPTION

In the following detailed description reference is made to theaccompanying drawings, which form a part hereof and in which areillustrated by way of illustration specific embodiments in which theinvention may be practiced. In this regard, directional terminology suchas “top”, “bottom”, “front”, “back”, “leading”, “trailing” etc. is usedwith reference to the orientation of the Figures being described. Sincecomponents of embodiments of the invention can be positioned in a numberof different orientations, the directional terminology is used forpurposes of illustration and is in no way limiting. It is to beunderstood that other embodiments may be utilized and structural orlogical changes may be made without departing from the scope defined bythe claims.

The description of the embodiments is not limiting. In particular,elements of the embodiments described hereinafter may be combined withelements of different embodiments.

The terms “wafer”, “substrate” or “semiconductor substrate” used in thefollowing description may include any semiconductor-based structure thathas a semiconductor surface. Wafer and structure are to be understood toinclude silicon, silicon-on-insulator (SOI), silicon-on sapphire (SOS),doped and undoped semiconductors, epitaxial layers of silicon supportedby a base semiconductor foundation, and other semiconductor structures.The semiconductor need not be silicon-based. The semiconductor could aswell be silicon-germanium, germanium, or gallium arsenide. According toother embodiments, silicon carbide (SiC) or gallium nitride (GaN) mayform the semiconductor substrate material.

As employed in this specification, the terms “coupled” and/or“electrically coupled” are not meant to mean that the elements must bedirectly coupled together—intervening elements may be provided betweenthe “coupled” or “electrically coupled” elements. The term “electricallyconnected” intends to describe a low-ohmic electric connection betweenthe elements electrically connected together.

The terms “lateral” and “horizontal” as used in this specificationintends to describe an orientation parallel to a first surface of asemiconductor substrate or semiconductor body. This can be for instancethe surface of a wafer or a die.

The term “vertical” as used in this specification intends to describe anorientation which is arranged perpendicular to the first surface of thesemiconductor substrate or semiconductor body.

FIG. 1A shows a cross-sectional view of an integrated circuit accordingto an embodiment. The integrated circuit 1 illustrated in FIG. 1Acomprises a battery 2 and integrated circuit elements 170. Theintegrated circuit elements 170 may comprise conductive lines 171 andfurther devices, such as active or passive semiconductor devices 172including resistors, transistors and further elements. The integratedcircuit elements 170 may additionally comprise devices for generatingelectrical power. Further, the integrated circuit elements 170 maycomprise components for performing a special function such as sensorelements including e.g. current sensors, voltage sensors and others.

The battery 2 comprises an anode 11 and a cathode 12 as well as anelectrolyte 130. The battery 2 comprises a housing including a firstsubstrate 100 and a lid 200. A cathode material 210 may be disposed atthe lid to form the cathode 12. For example, the battery may beimplemented as a lithium ion battery in which the anode comprises acomponent made of a semiconductor material such as silicon.

The anode 11 may comprise silicon material which may be monocrystalline,polycrystalline or amorphous. The silicon material may be doped with anydopant as is conventionally used such as boron (B), arsenic (As),phosphorous (P), antimony (Sb), gallium (Ga), indium (In) or selenium(Se). The active silicon surface of the anode 11 may be planar orpatterned. For example, three-dimensional structures such as pyramids,trenches and columns may be formed in the surface of the anode 11. Athin metal layer (not shown) may be formed over the surface of the anode11, the thin metal layer being in contact with the electrolyte 130. Forexample, the metal layer may comprise silver (Ag), aluminum (Al), gold(Au), palladium (Pd) or platinum (Pt). Metals forming an alloy withlithium may be used. Further examples comprise Zn, Cd, B, Ga, In, Th, C,Si, Ge, Sn, Pb, As, Sb, Bi, Se, and Te. A thickness of the metal layer11 may be less than 100 nm and more than 1 nm. Therefore, when applyingan Ag metal layer, an Ag—Li alloy will be formed at the surface of theanode 11 before charging the Si material with lithium so that the Liions will move to the Si anode in a homogeneous manner. Further, due tothe alloy layer, the formation of the native SiO₂ layer on the anodesurface is prevented so that the transportation of ions is furtherenhanced. In addition, the incorporation of Li atoms into the Si anodewill be accomplished in a more homogeneous manner so that theperformance of the lithium ion battery will be improved. Moreover, dueto the presence of the thin metal layer, the mechanical stability of theelectrode during charging and discharging is enhanced.

The cathode 12 may be made of one or more cathode materials 210. As acathode material 210, generally known electrochemical materials that areused in lithium ion batteries may be employed. Example comprise LiCoO₂,LiNiO₂, LiNi_(1-x)Co_(x)O₂, Li(NiO_(0.85)CO_(0.1)Al_(0.05))O₂,Li(Ni_(0.33)CO_(0.33)Mn_(0.33))O₂, LiMn₂O₄ spinel and LiFePO₄.

The electrolyte 130 may include electrolyte salts commonly used forlithium batteries such as e.g. LiPF₆, LiBF₄ or salts which do notinclude fluorine such as LiPCl₆, LiClO₄ in water-free aprotic solventssuch as propylene carbonate, dimethyl carbonate or 1,2-dimethoxymethane,ethylene carbonate, diethyl carbonate and others, polymers, for examplepolyvinylidene fluoride (PVDF) or other polymers, solid electrolytessuch as Li₃PO₄N and others. For example, liquid electrolytes may beused, for example, electrolytes that do not withstand high temperaturesthat are higher than 80° C. As is to be clearly understood, also solidor liquid electrolytes that withstand temperatures higher than 80° C.may be used. As will become apparent from the following description, iffluorine-free salts and fluorine-free solvents are used as electrolytes,problems may be avoided when the housing of the lithium ion batteryincludes components made of glass.

The separator element 135 spatially and electrically separates the anode11 and the cathode 12 from each other.

The separator element 135 should be permeable for the ions so that aconversion of the stored chemical energy into electrical energy may beaccomplished. Examples of the material of the separator element 135comprise non-woven fabric made of materials such as fiber glass,polyethylene or microporous materials. Further, membranes which are madeof microporous sheet that may comprise several layers may be employed.Further examples comprise non-woven fabric which is coated with aceramic material. As is to be clearly understood, the separator element135 may be dispensed with.

The battery 2 may be a rechargeable or secondary lithium ion battery.According to a further embodiment, the battery may be a primary batterywhich is not rechargeable. The battery 2 shown in FIG. 1 has an improvedcapacity for energy storage, since silicon has a large capacity ofinsertion of lithium. In other words, the amount of lithium atoms thatcan be stored or inserted in silicon is much larger than in conventionalcases. Since—as will be discussed in the following—the first substratemay comprise a semiconductor material, general semiconductor processingmethods may be employed. In particular, methods for manufacturingminiaturized sizes can effectively be applied for manufacturing abattery having a small size in comparison to conventional batteries.Further, components of integrated circuits may be easily integrated withthe battery 2.

The battery 2 shown in FIG. 1A comprises a first substrate 100 having afirst main surface 110, a lid 200 comprising a conductive cover element205, the lid being attached to the first main surface 110 of the firstsubstrate 100. A cavity 126 is formed between the first substrate 100and the lid. The electrolyte 130 is disposed in the cavity 126. Theanode 11 of the battery is formed at the first substrate 100 and thecathode 12 of the battery is formed at the lid 200. The lid 200 may beattached to the first substrate 100 with an insulating layer 150disposed between the lid 200 and the first substrate 100. Thereby, theanode 11 and the cathode 12 may be insulated from each other. Accordingto a further example, the first substrate may be an insulatingsubstrate, including the anode that comprises a component made ofsilicon. A cavity 126 is disposed between the first substrate and thelid. For example, this may be accomplished by a depression 125 formed inthe first substrate 100. According to a further embodiment, anintermediate member such as a further substrate portion may be disposedbetween the first substrate and the lid to form the cavity 126.According to an implementation, the thickness of the insulating layer150 may be selected so that the cavity 126 is formed.

According to the embodiment shown in FIG. 1A, the lid 200 may be made ofa conductive material to form the conductive cover element. Theconductive cover element may be a conductive foil 205. The lid 200 ofFIG. 1A comprises a conductive foil 205 and a cathode material 210. Thecathode material 210 may be directly adjacent and in physical contactwith the conductive foil 205. According to an embodiment, a primer layeror an adhesive layer may be disposed between the conductive foil 205 andthe cathode material 210. The primer layer (not illustrated) may improveadhesion between the conductive foil 205 and the cathode material 210.The conductive foil 205 forms the top surface of the housing of thelithium ion battery 2. According to the embodiment shown in FIG. 1A, theconductive foil 205 may be a metal foil or any kind of a conductivemetal compound foil, e.g. a conductive metal oxide foil. Furtherexamples of the material of the conductive foil comprise metal alloys.In the present embodiment, the conductive foil 205 may be an aluminumfoil. The cathode material 210 is in contact with the electrolyte 130and implements a lithium source. The lid 200 is attached to the firstmain surface 110, wherein an insulating layer 150 is disposed betweenthe first substrate and an adhesive foil 160 for attaching the lid tothe first substrate 100. The adhesive foil may be a sealing tapecomprising a heat curable polymer. For example, the sealing tape may bean epoxy resin or may comprise a composite material which is commonlyused in the manufacture of Li batteries. For example, the conductivecover element may be an aluminum foil having a thickness of more thanapproximately 50 μm. Alternatively, the conductive cover element mayalso be a thin aluminum plate. According to a further embodiment, theconductive cover element may comprise copper that is coated with analuminium layer. A cathode material layer may be disposed on the secondsurface of the conductive foil 205. The cathode material layer may havea lateral extension which is smaller than the lateral extension of theconductive foil 205.

In the following, a method of manufacturing an integrated circuit shownin FIG. 1A will be illustrated by referring to FIGS. 1B and 1C. A firstsubstrate 100 which may comprise a semiconductor material or may be asemiconductor substrate, e.g. a silicon substrate, is prepared so as toestablish an anode of a lithium battery. In particular, a depression 125is formed, followed by trenches 225 so as to form a patterned surface.An insulating layer 150 having a thickness of about 100 nm to 5 μm isformed over the first surface 110 of the first substrate 100.Thereafter, a back side metallization (element) 140 may be formed on thesecond main surface 120 of the first substrate. The back sidemetallization 140 may comprise a metal layer such as aluminium, copperor a combination of these metals.

Then, an adhesive foil 160 is formed over the insulating layer 150. Forexample, the adhesive foil may comprise an epoxy resin or a suitablecomposite material including a heat curable polymer.

A cathode material layer 210 which may e.g. comprise NCA or any othercathode material as discussed above is formed on the second surface of aconductive foil 205. For example, the NCA layer 210 may be formed usinga screen printing method or drop casting with subsequent pressing. Asuitable electrolyte 130 is filled into the cavity 126.

The conductive foil 205 may be an aluminum foil, a copper foil or maycomprise any other materials suitable for forming a conductive coverelement as a component of the lid of a lithium battery. For example, theconductive foil may have a thickness of approximately 40 to 200 μm, forexample, to 100 μm. The metal of the conductive foil should becompatible with the lithium source. The thickness of the conductive foil205 is selected so that this foil has the required mechanical stability.An electrolyte is filled into the cavity 126 formed between the firstsubstrate 100 and the lid 200. The conductive foil 205 including thecathode material layer 210 is brought into contact with the adhesivefoil on the insulating layer 150 that is formed over the first mainsurface of the first substrate 100. Then, a thermal step is performed soas to bond the conductive foil 205 to the first substrate 100, theinsulating layer 150 being interposed. For example, a temperature duringthis thermal step may be 80 to 200° C., for example, 120 to 180° C.According to an implementation, the thermal step may be performed for ashort time only that is sufficient to enable bonding. In this case, theshort time will prevent the electrolyte from heating to a hightemperature.

FIG. 1C shows a cross-sectional view of an example of a resultingstructure. FIG. 1D shows a modification of the structure shown in FIG.1C. As is shown, the lithium ion battery may further comprise a barrierlayer (stack) that may be formed over portions of the anode. Forexample, the barrier layer may comprise a metal layer 112 such as TiW.Optionally, the barrier layer stack may further comprise an oxide layer113 such as silicon oxide. For example, such an oxide layer may beformed by a PECVD (plasma enhanced chemical vapour deposition) method.The barrier layer (stack) may prevent the diffusion of lithium into thesilicon at certain positions. The barrier layer (stack) may comprise ametallic layer alone or in combination with another metallic or oxidelayer. As is illustrated in FIG. 1D, the barrier layer (stack) may bedisposed in the trenches 225. According to the modification shown inFIG. 1E, the barrier layer (stack) may be disposed in the trenches 225and in the silicon pillars between adjacent trenches 225. Differentlystated, according to the modification shown in FIG. 1E, the barrierlayer (stack) is disposed over horizontal portions of the anode 11. Asis to be clearly understood, the barrier layer (stack) may be combinedwith any of the embodiments described herein.

FIG. 2A shows a further embodiment of an integrated circuit. Differingfrom the embodiment shown in FIG. 1A, the lid 400 comprises a secondsubstrate 420 and a conductive cover element 405. The conductive coverelement 405 is attached to a first main surface 421 of the secondsubstrate 420. Further, a recess 425 is formed in the second substrate420. Accordingly, the combined structure of the lid 400 and the firstsubstrate includes a cavity 326. The recess 425 shown in FIG. 2A isfilled with e.g. NCA as a lithium source to form the cathode 12.Further, an electrolyte 130 is disposed within the cavity 326, theelectrolyte 130 being separated from the NCA 430 by means of theseparator element 135. According to the embodiment shown in FIG. 2A, theconductive cover element 400 forms the top surface of the housing of thelithium battery.

The integrated circuit shown in FIG. 2A further comprises integratedcircuit elements 370 such as conductive lines 371 and further devices372 as has been explained with reference to FIG. 1A. The integratedcircuit illustrated in FIG. 2A may further comprise the barrier layer(stack) that has been explained with reference to FIGS. 1D and 1E.

In the following, a method of manufacturing the integrated circuit ofFIG. 2A will be explained by referring to FIGS. 2B to 2F.

A second substrate 420 is patterned to include a recess 425. Forexample, the second substrate may be made of an insulating material suchas glass for a suitable polymer. According to a further embodiment, thesecond substrate 420 may be made of a semiconductor material. If thesecond substrate 420 is made of an insulating material, a furtherinsulating layer between the first substrate 300, at which the anode isto be formed, and the second substrate 420 may be dispensed with.Accordingly, the lid 400 may be directly attached to the first substrate300. For defining the recess 425 in the second substrate, a hard masklayer is formed on a first main surface 421 and on the second mainsurface 422 of the second substrate. For example, the hard mask layermay comprise any suitable hard mask material. The hard mask layer on thesecond main surface 422 of the second substrate may be patterned. (FIG.2B)

Thereafter, an etching step may be performed to etch material from thesecond main surface 422. The recess 425 may extend from the second mainsurface 422 to the first main surface 421. Thereafter, the residues ofthe hard mask layer are removed from the first and the second surfaces421, 422. A cross-sectional view of a resulting structure is shown inFIG. 2C.

Then, a conductive cover element 405 is formed over the recess 425. Forexample, a metal foil or a metal plate may be attached to the first mainsurface 421 of the second substrate 420. According to an example, themetal foil or the metal plate may be made of aluminum. For example, theadhesive used for attaching the conductive cover element 405 to thefirst main surface 421 may be a UV or thermally curable adhesive. Thelateral extension of the conductive cover element 405 may be smallerthan the lateral extension of the second substrate 420. For example,this may be accomplished by selecting a metal foil or metal plate havinga smaller lateral extension. Alternatively, the conductive cover element405 may be applied to the second substrate 420 followed by an etchingstep for removing the conductive cover element from an edge portion ofthe second substrate 420 to uncover a portion of the first main surface421 of the second substrate 420. FIG. 2D shows a cross-sectional view ofa resulting structure.

Thereafter, the recess 425 is filled with the cathode material, e.g. NCAthat may, for example, be applied using a screen printing method. FIG.2E shows an example of a resulting structure.

A first substrate 300 which may comprise a semiconductor material or maybe a semiconductor substrate, e.g. a silicon substrate, is prepared soas to establish an anode of a lithium battery. In particular, adepression 325 is formed, followed by trenches 326 so as to form apatterned surface. A back side metallization (element) 340 may be formedon the second main surface 320 of the first substrate.

An electrolyte is filled into the cavity 326 formed between firstsubstrate and the conductive cover element 405. In a next step, thesecond substrate 420 including the conductive cover element 405 isattached to the first substrate 300, for example, using a UV curableadhesive as indicated by the downward facing arrows in FIG. 2F. Sincethe conductive cover element 405 has a lateral extension smaller than alateral extension of the second substrate 420, an edge portion of thesecond substrate 420 is not covered by the conductive cover element. Asa result, this portion of the second substrate 420 is transparent to UVradiation so that the cavity 326 may be closed using a UV curableadhesive. Hence, the lid 400 may be bonded to the first substrate 300without applying a high temperature, whereby the electrolyte isprevented from being degraded due to applied heat.

According to the embodiment described, the conductive cover elementforms the top element of the lid and is in contact with a cathodematerial. Hence, a vertical connection between the anode 11 and thecathode 12 may be provided.

FIG. 3 illustrates a general method of manufacturing a lithium battery.The method comprises attaching a lid to a first main surface of a firstsubstrate (S140), the lid comprising a conductive cover element, forminga cavity between the lid and the first substrate (S100), forming ananode comprising a component made of silicon at the first substrate(S110), forming a cathode (S120) of the battery at the lid, and fillingan electrolyte into the cavity (S130). According to an embodiment,forming the lid may comprise attaching a conductive layer to a firstmain surface of a second substrate (S90). The exact succession of thesteps may depend from the requirements when manufacturing the battery.As is to be clearly understood, the steps may be performed in adifferent order.

According to a further embodiment, the structure shown in FIGS. 1A and2A may be manufactured using alternative manufacturing methods employinga higher temperature. For example, in case of no thermal budgetlimitation, alternative wafer bonding techniques may be used for theformation of the cavity such as anodic bonding, diffusion bonding,eutectic bonding etc. According to these methods, a stable and hermeticenclosure system between the different substrates may be formed. Due tothe presence of the lid comprising a conductive cover element, avertical and/or horizontal electrical connection to the lithium ionelectrochemical system may be accomplished.

According to the embodiments described above, the integrated circuit 1comprises a battery 2 and integrated circuit elements 170, 370.Components of the battery and the integrated circuit elements maydisposed on the same semiconductor substrate or semiconductor chip.According to further embodiments, the battery and elements of anelectric circuit may be disposed on separate semiconductor substrates orchips. When the battery and the electric circuit are disposed onseparate chips, the battery may be electrically coupled to the electriccircuit via an interconnection.

Generally, within the context of the present specification, the electriccircuit or the integrated circuit may comprise a processing device forprocessing data. The electric circuit or the integrated circuit mayfurther comprise one or more display devices for displaying data. Theelectric circuit or the integrated circuit may further comprise atransmitter for transmitting data. The electric device or the integratedcircuit may further comprise components which are configured toimplement a specific electronic system. According to an embodiment, theelectric device or the integrated circuit may further comprise an energyharvesting device that may deliver electrical energy to the battery 2,the energy having been generated from solar, thermal, kinetic or otherkinds of energy. For example, the electric device or the integratedcircuit may be a sensor such as a tire pressure sensor, wherein theelectric circuit or the integrated circuit further comprises sensorcircuitry and, optionally, a transmitter that transmits sensed data toan external receiver. According to another embodiment, the electricdevice or the integrated circuit may be an actuator, an RFID tag or asmartcard. For example, a smartcard may additionally comprise afingerprint sensor, which may be operated using energy delivered by thebattery 2.

While embodiments of the invention have been described above, it isobvious that further embodiments may be implemented. For example,further embodiments may comprise any subcombination of features recitedin the claims or any subcombination of elements described in theexamples given above. Accordingly, the spirit and scope of the appendedclaims should not be limited to the description of the embodimentscontained herein.

What is claimed is:
 1. A lithium ion battery, comprising: a firstsubstrate having a first main surface; a lid comprising a conductivecover element, the lid being attached to the first main surface; acavity formed between the first substrate and the lid; an electrolytedisposed in the cavity; an anode comprising a component made of asemiconductor material at the first substrate; and a cathode at the lid.2. The lithium ion battery according to claim 1, wherein the lid is madeof a conductive material to form the conductive cover element.
 3. Thelithium ion battery according to claim 1, further comprising aninsulating layer between the first substrate and the lid.
 4. The lithiumion battery according to claim 1, wherein: the lid further comprises asecond substrate, the conductive cover element being attached to a firstmain surface of the second substrate; a recess is defined in the secondsubstrate; and the second substrate is attached to the first mainsurface of the first substrate.
 5. The lithium ion battery according toclaim 2, wherein the conductive cover element is a conductive foil. 6.The lithium ion battery according to claim 4, wherein the conductivecover element is a conductive foil.
 7. The lithium ion battery accordingto claim 4, wherein the recess is formed so as to uncover a second mainsurface of the conductive cover element.
 8. The lithium ion batteryaccording to claim 1, wherein the semiconductor material is silicon. 9.An integrated circuit formed in a first semiconductor substrate having afirst main surface, the integrated circuit comprising a lithium ionbattery further including: a lid comprising a conductive cover element,the lid being attached to the first main surface; a cavity formedbetween the first semiconductor substrate and the lid; and anelectrolyte disposed in the cavity; and an anode comprising a componentmade of a semiconductor material at the first semiconductor substrate, acathode at the lid.
 10. A method of manufacturing a lithium ion battery,the method comprising: attaching a lid to a first main surface of afirst substrate, the lid comprising a conductive cover element; forminga cavity between the lid and the first substrate; forming an anodecomprising a component made of a semiconductor material at the firstsubstrate; forming a cathode at the lid; and filling an electrolyte intothe cavity.
 11. The method according to claim 10, wherein the lid isattached to the first main surface of the first substrate after fillingthe electrolyte into the cavity.
 12. The method according to claim 10,wherein forming the anode comprises patterning the first substrate toform grooves.
 13. The method according to claim 10, wherein forming thelid comprises providing a metal foil.
 14. The method according to claim10, wherein the lid is attached to the first main surface of the firstsubstrate by a method selected from the group consisting of thermalbonding, bonding using UV curable adhesive and anodic bonding.
 15. Themethod according to claim 10, wherein forming the lid comprisesattaching a conductive cover element to a first main surface of a secondsubstrate.
 16. The method according to claim 15, wherein a lateralextension of the conductive cover element is selected so that an edgeportion of the second substrate is uncovered.
 17. The method accordingto claim 15, wherein the second substrate is made of an insulatingmaterial.
 18. The method according to claim 16, wherein the lid isattached to the first main surface of the first substrate by bondingusing UV curable adhesive, wherein UV radiation is transmitted throughthe uncovered edge portion of the second substrate.
 19. The methodaccording to claim 16, wherein forming a recess in the lid comprisesforming a recess in the second substrate.